Plate-like particle of cathode active material for lithium secondary battery, cathode of the lithium secondary battery and lithium secondary battery

ABSTRACT

To provide a lithium secondary battery which has high capacity while maintaining excellent charge-discharge characteristic, and to provide a cathode of the lithium secondary battery and a plate-like particle for cathode active material to be contained in the cathode. The plate-like particle of cathode active material for a lithium secondary battery of the present invention has a layered rock salt structure, a thickness of 5 μm or more and less than 30 μm, 2 or less of [003]/[104] which is a ratio of intensity of X-ray diffraction by the (003) plane to intensity of X-ray diffraction by the (104) plane, a voidage of 3% or more and less than 30%, and an open pore ratio of 70% or higher.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a plate-like particle of cathode active material for lithium secondary battery, a cathode of a lithium secondary battery and a lithium secondary battery.

2. Description of the Related Art

A cathode active material for lithium secondary battery (may be referred to as a lithium ion secondary cell) using a plate-like particle of a lithium composite oxide (lithium transition metal oxide) having a layered rock salt structure is well-known (e.g., Japanese Patent Application Laid-Open (kokai) No. Hei 5-226004).

With respect to this kind of the plate-like particle, charge and discharge characteristics can be enhanced by means of exposure of the crystal plane through which lithium ions are intercalated and deintercalated (for example, the (104) plane) as much extent as possible to a plate surface. Also, filling ratio of cathode active material in a cathode can be raised and high capacity can be achieved by enlarging size (for example, to the extent of 5 μm or more and less than 30 μm in thickness) of the plate-like particle.

Meanwhile, impairment of capacity by repetition of charge-discharge cycles (may be referred to as impairment of cyclic characteristic) can occur in this kind of the lithium secondary battery. In order to elucidate the cause for the impairment, the cathode tested in an experiment example where the cyclic characteristic had been impaired were previously observed under an electron microscope. Through observation, cracks were found to be generated at the grain boundary in the plate-like particles (hereinafter, the cracks are referred to as “grain boundary cracks”). Furthermore, separation was found between a binder which contained an electroconducting aid such as carbon and the plate-like particles which were dispersed in the binder (hereinafter, the separation is referred to as “interface separation”).

The grain boundary crack and the interface separation are thought to be caused by crystal lattice expansion/contraction associated with intercalation and deintercalation of lithium ions in charge-discharge cycles, wherein the crystal lattice expansion/contraction includes the expansion/contraction of volume and the expansion/contraction not involving change in volume. Thus, such grain boundary crack or interface separation, which results in generation of an electrically isolated portion (i.e., a portion which does not contribute to capacity) through breakage of an electrical conduction path in a cathode active material layer, to thereby reduce capacity, is thought to be a possible cause for deterioration in cycle characteristic.

SUMMARY OF THE INVENTION

The present invention has conceived in order to solve the aforementioned problems. That is, an object of the present invention is to provide a lithium secondary battery which has high capacity while maintaining excellent charge-discharge characteristic. Another object of the invention is to provide a cathode of the lithium secondary battery and a plate-like particle for cathode active material to be contained in the cathode.

<Configuration>

The plate-like particle of cathode active material for lithium secondary battery of the present invention (hereinafter may optionally be referred to simply as “plate-like particle”) has a layered rock salt structure. The cathode of the lithium secondary battery of the present invention (hereinafter may be referred to simply as “cathode”) has a cathode active material layer which contains the plate-like particles. Specifically, the cathode active material layer may be formed by dispersing the plate-like particles and the electroconducting aid in the binder. The lithium secondary battery of the present invention is comprised of the cathode; an anode which contains a carbonaceous material or a lithium-occluding material as anode active material; and an electrolyte provided so as to intervene between the positive electrode and the negative electrode.

“The term layered rock salt structure” of the plate-like particle of cathode active material for lithium secondary battery of the present invention refers to a crystal structure in which lithium layers and layers of a transition metal other than lithium are arranged in alternating layers with an oxygen layer therebetween; i.e., a crystal structure in which transition metal ion layers and lithium layers are arranged in alternating layers via oxide ions (typically, α-NaFeO₂ type structure: structure in which a transition metal and lithium are arrayed orderly in the direction of the axis of cubic rock salt type structure). The plate-like particle is typically comprised of lithium composite oxide. As used herein, the term “lithium composite oxide” refers to an oxide represented by LixMO₂ (0.05<x<1.10, M is at least one transition metal (typically, M includes one or more species of Co, Ni, and Mn)).

A characteristic feature of the present invention resides in that the plate-like particle has a thickness of 5 μm or more and less than 30 μm, peak intensity ratio [003]/[104] is 2 or less, a voidage of 3 to 30%, and an open pore ratio of 70% or more. As used herein, peak intensity ratio [003]/[104] is the ratio of intensity of diffraction by the (003) plane to intensity of diffraction by the (104) plane.

Generally, the plate-like particle may be formed so as to have a ratio w/t of 3 or more, wherein t represents the thickness of the plate-like particle, and w represents the minimum size in the plate surface direction (direction orthogonal to the thickness direction).

The term “thickness direction” refers to the direction which defines the “thickness” t of the plate-like particle; typically, a direction parallel with the vertical direction in a state in which the plate-like particle is placed stably on a horizontal surface. The term “thickness” refers to the size of the plate-like particle as measured in the “thickness direction.”

The term “plate surface” refers to a surface of the plate-like particle which is orthogonal or nearly orthogonal to the “thickness direction” of the sheet. Since the “plate surface” of the plate-like particle is the widest surface on the sheet, the “plate surface” may be referred to as the “principal surface.” The term “plate surface direction” refers to a direction parallel with the “plate surface” (i.e., in-plane direction). Thus, the “thickness” of the plate-like particle is equivalent to the shortest distance between the generally parallel two plate surfaces of the sheet. The aforementioned “thickness direction” is the direction which defines the shortest distance between the two “plate surfaces.”

Specifically, the thickness t of the plate-like particle is determined by, for example, measuring the distance between the generally parallel plate surfaces as observed in cross section under an SEM (scanning electron microscope). The minimum size in the plate surface direction “w” is determined by, for example, taking a plan view of the plate-like particle under an SEM, and measuring the diameter of the inscribed circle of the contour of the plan view.

As used herein, the term “voidage” refers to the volume proportion of voids (pores: including open pores and closed pores) in the plate-like particle of the present invention. “Voidage” may also be referred to as “porosity.” “Voidage” is calculated from, for example, bulk density and true density of the plate-like particle.

As used herein, the term “open pore ratio” refers to the ratio by volume of open pores to all the voids (pores) contained in the sintered lithium composite oxide sheet of the present invention. As used herein, the term “open pore” refers to a pore which is contained in the sintered lithium composite oxide sheet of the present invention and which communicates with the outside of the cathode active material. “Open pore ratio” may be calculated from the total volume of open pores and closed pores determined by bulk density, and the volume of closed pores determined by apparent density. In this case, parameters used for calculation of “open pore ratio” may be determined through, for example, Archimedes' method.

When the plate-like particle has a structure in which numerous primary particles (crystal particles) have been bound to one another, the primary particles preferably have a size (primary particle size) of 5 μm or less.

<Action and Effect>

The plate-like particle has a thickness of 5 μm or more but less than 30 μm and peak intensity ratio [003]/[104] is 2 or less (preferably 2 or less, more preferably 1.2 or less, still more preferably 0.6 or less). Then, filling ratio of cathode active material in the cathode active material layer can be raised, and the crystal plane through which lithium ions are intercalated and deintercalated (for example, the (104) plane) can expose to a plate surface as much extent as possible. Therefore, high capacity and enhanced charge-discharge characteristic can be achieved. Additionally, cycle characteristic can be improved by above-mentioned mean pore size, voidage, and 2 or less in peak intensity ratio [003]/[104]. One possible reason for the improvement may be as follow.

The crystal lattice expansion/contraction (expansion/contraction in volume) associated with charge-discharge cycles occurs to the highest extent in a direction normal to the (003) plane (i.e., [003] direction). Therefore, grain boundary cracks caused by crystal lattice expansion/contraction associated with charge-discharge cycles readily occurs in a direction parallel to the (003) plane. Furthermore, the (003) plane is a closest packing plane in terms of oxygen and does not allow lithium ions and electron to enter and exit the crystal lattice. Thus, the (003) plane is a chemically and electrochemically inert plane.

In this regard, as described above, when the peak intensity ratio [003]/[104] is 2 or less, there is reduced the ratio of the (003) plane which is developed to a plate surface of the plate-like particle, or the ratio of the (003) plane which is oriented in the direction parallel to the plate surface in the plate-like particle. Because of this, grain boundary crack occurring in a direction parallel to the plate surface, which would impair inter alia the capacity, can be effectively prevented. Also, the bonding strength increased at the bonding interface with the binder, to thereby prevent interface separation.

Also, as described above, the plate-like particle includes pores having a specific state at a specific ratio. Therefore, the stress generated by crystal lattice expansion/contraction associated with intercalation and deintercalation of lithium ions in charge-discharge cycles is favorably (uniformly) released by the pores. As a result, grain boundary crack associated with repeated charge-discharge cycles can be prevented to the possible extent. In addition, by virtue of the pores (open pores) present at the bonding interface with the binder, the bonding strength is enhanced. As a result, deformation of the plate-like particle caused by crystal lattice expansion/contraction associated with intercalation and deintercalation of lithium ions in charge-discharge cycles can be prevented, whereby the aforementioned interface separation is more favorably prevented.

Particularly when the open pore ratio is adjusted to 70% or higher, stress is more easily released, to thereby effectively prevent grain boundary cracking. One conceivable reason therefor is as follows. As described above, volume expansion/contraction in the cathode is caused by intercalation and deintercalation of lithium ions in crystal lattice. The open pore is surrounded by a face through which intercalation and deintercalation of lithium ions occur. Thus, the open pore is thought to exhibit a stress releasing effect higher than that of the closed pore. In addition, through controlling the open pore ratio to 70% or higher, the aforementioned interface separation is effectively prevented. One conceivable reason therefor is as follows. An open pore is thought to be equivalent to surface roughness. Through incorporation of open pores, surface roughness increases, whereby bonding strength is enhanced by a so-called anchor effect.

Furthermore, through incorporation of electrolyte, conductive material, or the like into an open pore, the inner wall of the open pore favorably serves as a lithium ion intercalation/deintercalation face. Therefore, controlling the open pore ratio to 70% or higher is also preferred, since the rate characteristic is improved, as compared with the case of a high closed pore ratio, the closed pore being present as a simple pore (i.e., a portion which does not contribute to charge-discharge).

Meanwhile, when the mean pore size is in excess of 5 μm, relatively large pores are provided. Such larger pores are generally not in the form of complete sphere but in the form of deformed sphere. Therefore, stress concentration is likely to occur locally in the larger pores, and the effect of uniformly releasing the stress in the particle is difficult to attain. When the mean pore size is less than 0.1 μm or the voidage is less than 3%, the stress releasing effect by the pores is insufficient. Thus, in both cases, grain boundary crack is not satisfactorily prevented. Furthermore, in both cases, the effect of enhancing the bonding strength to the binder is impeded, and above-mentioned interface separation is not satisfactorily prevented.

As stated above, according to the present invention, the capacity can be enhanced, while favorable charge-discharge characteristics including cycle characteristic are maintained.

In contrast, when the voidage is lower than 3%, the stress releasing effect by pores is insufficient, whereas when the voidage is in excess of 30%, high capacity fails to be attained. Both cases are not preferred.

For example, lithium cobaltate expands its volume upon charge (i.e., deintercalation of lithium ions), whereas lithium nickelate expands its volume upon discharge (i.e., intercalation of lithium ions). Therefore, volume expansion/contraction upon charge-discharge cycles can be apparently reduced to zero by appropriately adjusting the compositional proportion of cobalt or nickel. However, even in this case, lattice length changes. Specifically, Li(Co_(0.5)Ni_(0.5))O₂ expands in a c-axis direction and contracts in an a-axis direction.

Therefore, the present invention is very effectively applied to the plate-like particle having the following composition: a lithium composite oxide having a layered rock salt structure (e.g., lithium cobaltate Li_(p)CoO₂ [wherein 1≦p≦1.1], lithium nickelate LiNiO₂, lithium manganate Li₂MnO₃, lithium nickel manganate Li_(p)(Ni_(0.5), Mn_(0.5))O₂, a solid solution thereof represented by the formula Li_(p)(Co_(x), Ni_(y), Mn_(z))O₂ [wherein 0.97≦p≦1.07, x+y+z=1], Li_(p)(Co_(x), Ni_(y), Al_(z))O₂ [wherein 0.97≦p≦1.07, x+y+z=1, 0<x≦0.25, 0.6≦y≦0.9, 0<z≦0.1], or a solid solution of Li₂MnO₃ and LiMO₂ (M is a transition metal such as Co or Ni)). The plate-like particle of the present invention may contain one or more elements selected from among, for example, Mg, Al, Si, Ca, Ti, V, Cr, Fe, Cu, Zn, Ga, Ge, Sr, Y, Zr, Nb, Mo, Ag, Sn, Sb, Te, Ba, and Bi, so long as any of the aforementioned formulas is satisfied.

Also, the present invention is particularly effectively applied to the case of a composition exhibiting increased volume expansion/contraction; for example, Li_(p)(Co_(x), Ni_(y), Mn_(z))O₂ wherein the proportion by mole of nickel is 0.75 or more or the proportion by mole of cobalt is 0.9 or more, or Li_(p)(Co_(x), Ni_(y), Al_(z))O₂ wherein the proportion by mole of nickel is 0.7 or more.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a sectional view of the schematic configuration of an embodiment of the lithium secondary battery of the present invention;

FIG. 2 is an enlarged sectional view of the cathode shown in FIG. 1;

FIG. 3 is an enlarged perspective view of a plate-like particle of cathode active material shown in FIG. 2;

DETAILED DESCRIPTION OF THE INVENTION

Preferred embodiments of the present invention will next be described with reference to examples and comparative examples. The following description of the embodiments is nothing more than the specific description of mere example embodiments of the present invention to the possible extent in order to fulfill description requirements (descriptive requirement and enabling requirement) of specifications required by law. Thus, as will be described later, naturally, the present invention is not limited to the specific configurations of embodiments and examples to be described below. Modifications that can be made to the embodiments and examples are collectively described herein principally at the end, since insertion thereof into the description of the embodiments would disturb understanding of consistent description of the embodiments.

<Configuration of Lithium Secondary Battery>

FIG. 1 is a sectional view of the schematic configuration of an lithium secondary battery 10 to which an embodiment of the present invention is applied. Referring to FIG. 1, the lithium secondary battery 10 of the embodiment has a cell casing 11, a separator 12, an electrolyte 13, an anode 14, and a cathode 15.

The separator 12 is provided so as to halve the interior of the cell casing 11 into the anode 14 section and the cathode 15 section. That is, the anode 14 and the cathode 15 are provided within the cell casing 11 in such a manner as to face each other with the separator 12 located therebetween. The cell casing 11 accommodates the electrolyte 13.

The electrolyte 13 which may be in the present invention is preferably a liquid electrolyte from the viewpoints, for example, electrical characteristics and easy handlability. The liquid electrolyte which may be employed in the present invention is preferably a nonaqueous-solvent-type which is prepared by dissolving an electrolyte salt such as a lithium salt in a nonaqueous solvent such as an organic solvent. The electrolyte 13 may be a polymer electrolyte, a gel electrolyte, an organic solid electrolyte, or an inorganic solid electrolyte, and no problem arises when such an electrolyte is employed.

No particular limitation is imposed on the solvent for the nonaqueous electrolytic solution. Examples of the solvent include chain esters, such as dimethyl carbonate, diethyl carbonate, ethyl methyl carbonate, and methyl propione carbonate; cyclic esters having high dielectric constant, such as ethylene carbonate, propylene carbonate, butylene carbonate, and vinylene carbonate; and mixed solvents of a chain ester and a cyclic ester. Among them, a mixed solvent containing a chain ester serving as a main solvent with a cyclic ester is particularly preferred.

Examples of the electrolyte salt to be dissolved in the above-mentioned nonaqueous solvent include LiClO₄, LiPF₆, LiBF₄, LiAsF₆, LiSbF₆, LiCF₃SO₃, LiC₄F₉SO₃, LiCF₃CO₂, Li₂C₂F₄(SO₃)₂, LiN(RfSO₂)(Rf′SO₂), LiC(RfSO₂)₃, LiC_(n)F_(2n+1)SO₃ (n≧12), and LiN(RfOSO₂)₂ [Rf and Rf′ each represent a fluoroalkyl group]. They may be used singly or in combination of two or more species.

Among the above-mentioned electrolyte salts, a fluorine-containing organic lithium salt having a carbon number of 2 or greater is particularly preferred. This is because the fluorine-containing organic lithium salt is high in anionic property and readily undergoes electrolytic dissociation, and is thus readily dissolvable in the above-mentioned solvent. No particular limitation is imposed on the electrolyte salt concentration of the nonaqueous electrolytic solution (electrolyte 13). However, for example, the concentration is 0.3 mol/L to 1.7 mol/L, more preferably 0.4 mol/L to 1.5 mol/L.

Any anode active material may be used in the anode 14, so long as the material can occlude and release lithium ions. For example, there may be used carbonaceous materials (e.g., graphite, pyrolytic carbon, coke, glassy carbon, a fired product of organic polymer compound, mesocarbon microbeads, carbon fiber, and activated carbon). Further, a portion of graphite may be replaced with a metal which can be alloyed with, for example, lithium or an oxide. Also, there may be used, as the anode active material, metallic lithium; an alloy which contains metallic lithium and another element (e.g., silicon, tin, or indium); an oxide of silicon, tin, or the like which can perform charge and discharge at low electric potential near that at which lithium does; and a lithium-occluding material such as a lithium cobalt nitride (e.g., Li_(2.6)Co_(0.4)N).

When graphite is employed as the anode active material, the voltage at full charge can be considered to be about 0.1 V (vs. lithium). Thus, the electric potential of the cathode 15 can be conveniently calculated as a cell voltage plus 0.1 V. Therefore, since the electric potential of the cathode 15 at charging is readily controlled, graphite is preferred.

FIG. 2 is an enlarged sectional view of the cathode 15 shown in FIG. 1. Referring to FIG. 2, the cathode 15 includes a cathode collector 15 a and a cathode active material layer 15 b. The cathode active material layer 15 b is comprised of a binder 15 b 1 and dispersed materials including a plate-like particle 15 b 2 of cathode active material and an electroconducting aid such as carbon, and is bonded to the cathode collector 15 a. The plate-like particle 15 b 2 of cathode active material of the present invention is composed of a sintered lithium composite oxide sheet and has a thickness of 5 μm or more and less than 30 μm, a voidage of 3 to 30%, and an open pore ratio of 70% or more.

FIG. 3 is an enlarged perspective view of the plate-like particle 15 b 2 of cathode active material shown in FIG. 2. As shown in FIG. 3, the plate-like particle 15 b 2 of cathode active material is formed such that a plane other than the (003) plane (e.g., the (101) plane or the (104) plane) is exposed at a plate surface (upper surface A and lower surface B: hereinafter, the “upper surface A” and the “lower surface B” are referred to as the “plate surface A” and the “plate surface B,” respectively), which is a surface normal to the thickness direction (the vertical direction in the drawings).

Specifically, the plate-like particle 15 b 2 of cathode active material of the present invention is formed such that the ratio of intensity of X-ray diffraction by the (003) plane to intensity of X-ray diffraction by the (104) plane; i.e., the peak intensity ratio [003]/[104] falls within a range of 2 or less. The (003) planes (colored black in the drawing) may be exposed at the end surfaces C, which intersect the plate surface direction (in-plane direction).

<Summary of Method for Producing the Plate-Like Particle of Cathode Active Material>

The plate-like particle 15 b 2 of cathode active material is readily and reliably formed through, for example, the following production method.

<<Two-Step Process>>

1. Preparation of Raw Material Particles

Particles of a transition metal (e.g., Co, Ni, or Mn) compound containing no lithium compound are employed as raw material particles. The raw material particles may be appropriately pulverized and classified. In consideration of a composition of interest, a plurality of types of raw material particles may be appropriately mixed together. The raw material particles may be mixed with a low-melting-point oxide (e.g., boron oxide, bismuth oxide, or antimony oxide), a low-melting-point chloride (e.g., sodium chloride or potassium chloride), or a low-melting-point glass material (e.g., borosilicate glass) in an amount of 0.001 to 30 wt. % for the purpose of promoting grain growth.

To the raw material particles, an additive for forming pores having a state and voidage of interest as mentioned above; i.e., a pore-forming material may be added, followed by uniformly mixing. The pore-forming material is preferably a particulate or fibrous substance which decomposes (vaporizes or is carbonized) in the subsequent calcination step. Specific examples of preferably employed pore-forming materials include theobromine, graphite, and organic synthetic resins such as nylon, phenolic resin, poly(methyl methacrylate), polyethylene, poly(ethylene terephthalate), and foamable resin, in the form of particle or fiber. Needless to say, if no such a pore-forming material is added, the pores having a size and voidage of interest as mentioned above can be formed through appropriately tuning the particle size of the raw material particles, the firing temperature employed in the calcination step, etc.

2. Raw Material Particle Sheet Forming Step

Raw material particles or a mixture thereof is subjected to a sheet forming step, to thereby form an “independent” sheet-like compact. As used herein, “independent” sheet (may be referred to as “self-standing film”) refers to a sheet which is independent of another support and can be handled by itself. The term “independent sheet-like compact” also means thin tablets having an aspect ratio of 5 or higher. Therefore, “independent” sheet does not include a sheet bonded to and integrated with another support (e.g., substrate) (i.e., impossible or difficult to separate from the support).

Sheet forming may be carried out through any well known technique. Specifically, sheet forming may be performed by means of, for example, a doctor blade-type sheet forming machine (doctor blade method), a drum dryer, a disk dryer, or a screen printing machine. The thickness of a sheet-like compact is appropriately determined so as to attain the aforementioned preferred thickness after firing.

3. Compact Calcination Step

The sheet-like compact formed through the aforementioned forming step is fired at a relatively low temperature (e.g., 700 to 1,200° C.) before the below-described lithium incorporation step. This calcination step forms a porous sheet-like intermediate fired compact containing numerous pores of relatively large size. This calcination step is carried out in air in a state where, for example, the above-formed sheet-like compact is placed on a zirconia-made embossed setter.

4. Lithium Incorporation Step

A lithium compound is applied to the intermediate fired compact obtained through the aforementioned calcination step, followed by thermal treatment, whereby lithium is incorporated into the intermediate fired compact. Thus, there is produced an “independent” sintered lithium composite oxide sheet for a cathode active material layer. The lithium incorporation step is carried out in, for example, a crucible.

Examples of the employable lithium compound include lithium salts such as lithium carbonate, lithium nitrate, lithium acetate, lithium peroxide, lithium hydroxide, lithium chloride, lithium oxalate, and lithium citrate; and lithium alkoxides such as lithium methoxide and lithium ethoxide. The lithium compound is added so that, in the sheet-like sintered compact represented by the formula Li_(x)MO₂, the ratio by mole of lithium to M (i.e., Li/M) is 1 or more.

When lithium is incorporated into the porous sheet-like intermediate fired compact yielded in the aforementioned calcination step, the pore size of the intermediate fired compact is decreases, whereby the aforementioned pores having a state and voidage of interest are formed.

5. Crushing Step

The above-mentioned sheet is crushed into a large number of plate-like particles before or after the above lithium incorporation step. For example, the crushing step may be performed by placing the above-mentioned sheet on a mesh having a predetermined mesh size and then press the sheet from above by a spatula.

<<One-Step Process>>

1. Preparation of Raw Material Particles

As raw material particles, there is used an appropriate particle mixture of compounds of Li, Co, Ni, Mn, etc. at such proportions that the formed cathode active material LiMO₂ has a layered rock salt structure. Alternatively, raw material particles having a LiMO₂ composition (synthesized) may also be used. To such raw material particles, the aforementioned pore-forming material is added.

In the below-mentioned thermal treatment step, a lithium compound may be added in an excessive amount of about 0.5 to about 30 mol % in order to promote grain growth or compensate for volatile matter. Also, for promoting grain growth, a low-melting-point oxide such as bismuth oxide or a low-melting-point glass such as borosilicate glass may be added in an amount of 0.001 to 30 wt. %.

2. Raw Material Particle Sheet Forming Step

Through subjecting a mixture of raw material particles and a pore-forming material to sheet forming, an “independent” sheet-like compact is produced. The sheet forming step is the same as the aforementioned two-step process.

3. Compact Thermal Treatment (Firing) Step

The sheet-like compact formed through the aforementioned forming step is thermally treated (fired) at a relatively high temperature (e.g., 1,200° C. to 1,500° C.) in order to proceed crystal growth with formation of pores, to thereby yield an “independent” sintered lithium composite oxide sheet for a cathode active material layer. This thermal treatment may be carried out in an oxygen atmosphere where, for example, the above-formed sheet-like compact is placed on a zirconia-made embossed setter.

4. Pulverization

The sheet obtained by the above-mentioned thermal treatment step was pulverized as stated above, to thereby produce plate-like particles 15 b 2 of cathode active material.

<Evaluation Method and Results>

For the evaluation of cell characteristics, a coin cell having the same shape as that of a type CR2032 cell was fabricated in the following manner.

The yielded positive electrode, a negative electrode formed from a lithium metal plate, stainless steel collector plates, and a separator were arranged in the order of collector plate-positive electrode-separator-negative electrode-collector plate. The resultant laminate was filled with an electrolytic solution, thereby yielding a coin cell. The electrolytic solution was prepared as follows: ethylene carbonate (EC) and diethyl carbonate (DEC) were mixed at a volume ratio of 1:1 so as to prepare an organic solvent, and LiPF₆ was dissolved in the organic solvent at a concentration of 1 mol/L.

The thus-fabricated coin cell was evaluated in terms of cycle characteristic (percent capacity maintenance).

Cycle Characteristic (Percent Capacity Maintenance):

The fabricated cell was subjected to cyclic charge-discharge at a test temperature of 20° C. The cyclic charge-discharge repeats: (1) charge at 1 C rate of constant current and constant voltage until 4.2 V is reached, and (2) discharge at 1 C rate of constant current until 3.0 V is reached. By dividing the discharge capacity of the cell as measured after the cyclic charge-discharge by the initial discharge capacity of the cell and being multiplied by 100, percent capacity maintenance (%) was obtained.

EXAMPLES

The present invention will next be described in more detail by way of specific examples of the above-mentioned plate-like particle 15 b 2 of cathode active material. Evaluations of the particles are also described.

Example 1

<<Specific Example 1: Cobalt-based composition>>

Producing conditions in Experiment Examples 1-1 to 1-9, where the plate-like particles 15 b 2 of cathode active material is LiCoO₂ ceramic particles, are shown in Table 1.

TABLE 1 Pore-forming Material Intermediate material particle size firing temp. shape/amount Process (μm) (° C.) (wt. parts) Exp. Ex. One-step fibrous/5 1-1 Exp. Ex. Two-step 0.3 1,100 0 1-2 Exp. Ex. Two-step 0.3 1,100 fibrous/5 1-3 Exp. Ex. Two-step 0.5 1,000 0 1-4 Exp. Ex. Two-step 1.0 1,000 fibrous/5 1-5 Exp. Ex. One-step fibrous/7.5 1-6 Exp. Ex. One-step fibrous/12.5 1-7 Exp. Ex. One-step fibrous/2.5 1-8 Exp. Ex. One-step spherical/5 1-9

The detailed production conditions employed in Experiment Examples 1-2 and 1-4 shown in Table 1 are as follows (two-step process, no pore-forming material).

(1) Preparation of Slurry

CO₃O₄ powder (particle size: 1 to 5 μm; product of Seido Kagaku Kogyo Co., Ltd.) was crushed and classified to prepare CO₃O₄ raw material powder. The CO₃O₄ raw material powder (100 parts by weight) was mixed with a dispersion medium (toluene:isopropanol=1:1) (100 parts by weight), a binder (polyvinyl butyral: product No. “BM-2,” product of Sekisui Chemical Co. Ltd.) (10 parts by weight), a plasticizer (DOP: di(2-ethylhexyl) phthalate, product of Kurogane Kasei Co., Ltd.) (4 parts by weight), and a dispersant (trade name “RHEODOL SP-O30,” product of Kao Corporation) (2 parts by weight). The resultant mixture was stirred under reduced pressure for defoaming, and the viscosity thereof was adjusted to 3,000 to 4,000 cP. The viscosity was measured by means of an LVT-type viscometer (product of Brookfield) in Specific Example 1 and other Examples.

(2) Sheet Forming

The thus-prepared slurry was formed into a sheet-like compact on a PET film through the doctor blade method so that the thickness of the compact as measured after drying was adjusted to 20 μm.

(3) Calcination

The sheet-like compact was removed from the PET film. 20 g of compact was crumpled and placed in a sheath made of alumina (dimensions: 150 mm square×10 mm in height), and then heated in air at a specific temperature (firing temperature for yielding an intermediate fired product) for 5 hours. Thereafter, the piece was cooled at 200 degrees (° C.)/h to room temperature. Then, a portion of the piece which was not fused to the sheath was picked up, to thereby produce flake-like fired compact.

(4) Pulverization

The thus-removed fired compact (50 g), nylon balls (diameter: 10 mm) (370 g), and ethanol (165 g) were placed in a polypropylene-made pot (volume: 1 L) and mixed for 20 hours for pulverization.

(5) Lithium Incorporation

The thus-obtained CO₃O₄ powder was mixed with Li₂CO₃ powder (product of Kanto Chemical Co., Inc.) so that Li/Co was 1.0, and the mixture was thermally treated in an oxygen atmosphere (0.1 MPa) at 760° C. for 20 hours, to thereby produce plate-like LiCoO₂ powder particles (plate-like particles 15 b 2 of cathode active material) having a thickness of 20 μm.

The detailed production conditions employed in Experiment Examples 1-3 and 1-5 shown in Table 1 are as follows (Two-step process, pore-forming material added).

A slurry was prepared through the same procedure employed in, for example, Experiment Example 1-2, except that a pore-forming material was added. As the pore-forming material, a fibrous material (Celish PC10S, product of Daicel FineChem LTd.) or a spherical material (Nylon powder, product of Sumitomo Environ Science) was employed. The thus-prepared slurry was formed into a sheet on a PET film in the same manner as employed in, for example, Experiment Example 1-2.

The sheet-like compact was removed from the PET film. 20 g of compact was crumpled and placed in a sheath made of alumina (dimensions: 150 mm square×10 mm in height), and then heated in air at 900° C. (firing temperature for yielding an intermediate fired product) for 10 hours. Thereafter, the piece was cooled at 200 degrees (° C.)/h. Then, a portion of the piece which was not fused to the sheath was picked up and pulverized. Lithium was incorporated into the thus-obtained CO₃O₄ ceramic powder in the same manner as employed in, for example, Experiment Example 1-2, to thereby produce plate-like LiCoO₂ powder particles (plate-like particles 15 b 2 of cathode active material) having a thickness of 20 μm.

The detailed production conditions employed in Experiment Examples 1-1 and 1-6 to 1-9 shown in Table 1 are as follows (One-step process).

(1) Preparation of Slurry

CO₃O₄ powder (particle size: 1 to 5 μm; product of Seido Kagaku Kogyo Co., Ltd.) was crushed and classified to prepare CO₃O₄ raw material powder. The CO₃O₄ raw material powder (particle size: 0.3 μm) was mixed with Li₂CO₃ powder (product of Kanto Chemical Co., Inc.) at a ratio Li/Co (mole) of 1.0. Thereafter, the aforementioned experiment procedure was repeated, except that the thus-obtained powder (100 parts by weight) and the aforementioned pore-forming material were employed, to thereby prepare a slurry (viscosity: 500 to 700 cP).

(2) Sheet Forming

The thus-prepared slurry was formed into a sheet-like compact on a PET film through the doctor blade method so that the thickness of the compact as measured after drying was adjusted to 20 μm.

(3) Calcination

The sheet-like compact was removed from the PET film. 20 g of compact was crumpled and placed in a sheath made of alumina (dimensions: 150 mm square×10 mm in height), and then heated in air at a specific temperature (firing temperature for yielding an intermediate fired product) for 5 hours. Thereafter, the piece was cooled at 200 degrees (° C.)/h to room temperature. Then, a portion of the piece which was not fused to the sheath was picked up, to thereby produce flake-like fired compact.

(4) Pulverization

The thus-removed fired compact (50 g), nylon balls (diameter: 10 mm) (370 g), and ethanol (165 g) were placed in a polypropylene-made pot (volume: 1 L) and mixed for 20 hours for pulverization, to thereby produce plate-like LiCoO₂ powder particles (plate-like particles 15 b 2 of cathode active material) having a thickness of 20 μm.

Table 2 shows the evaluation results of Experiment Examples shown in Table 1. In Table 2, the term “percent capacity maintenance” was obtained from the capacity after completion of 50 charge-discharge cycles. The “voidage” was obtained by dividing the bulk density of each sintered sheet (measured through the Archimedes' method) by the true density thereof (measured by means of a picnometer), to thereby obtain the relative density, and subtracting the relative density from 1. In the measurement of bulk density, the tested sintered sheet was boiled in water in order to sufficiently remove air remaining in the pores. When the sample had a small pore size, the pores of the sample were impregnated in advance with water by means of a vacuum impregnation apparatus (CitoVac, product of Struers), and the thus-treated sample was subjected to boiling treatment. The “open pore ratio” is a value calculated from the closed pore ratio and the total pore ratio [(open pore ratio)=(volume of open pores)/(total volume of all pores)=(volume of open pores)/(volume of open pores and closed pores). The closed pore ratio is calculated from an apparent density determined through the Archimedes' method. The total pore ratio is calculated from a bulk density determined through the Archimedes' method.

TABLE 2 Open pore Percent capacity Voidage ratio maintenance (%) (%) (%) Exp. Ex. 1-1 3.1 72 90 Exp. Ex. 1-2 3.2 83 91 Exp. Ex. 1-3 3 96 92 Exp. Ex. 1-4 7.6 82 91 Exp. Ex. 1-5 8.2 98 95 Exp. Ex. 1-6 14 71 91 Exp. Ex. 1-7 30 71 93 Exp. Ex. 1-8 2.7 72 40 Exp. Ex. 1-9 3.1 62 56

As is clear from Tables 1 and 2, the sintered sheets of Experiment Examples 1-1 to 1-7, which had a voidage of 3 to 30% and an open pore ratio of 70% or higher, exhibited excellent percent capacity maintenance, even after completion of 50 charge-discharge cycles. In contrast, the sintered sheet of Experiment Example 1-8, which had a voidage lower than the lower limit of the aforementioned range, and the sintered sheet of Experiment Example 1-9, which had an open pore ratio lower than the lower limit of the aforementioned range, exhibited considerably impaired cyclic characteristic (i.e., percent capacity maintenance after completion of 50 charge-discharge cycles). One possible reason therefor is as follows.

The sintered sheets of Experiment Examples 1-1 to 1-7 each include pores having a voidage falling within the aforementioned range at a specific proportion. Therefore, the stress generated by crystal lattice expansion/contraction associated with intercalation and deintercalation of lithium ions in charge-discharge cycles is favorably (uniformly) released. As a result, grain boundary cracking associated with charge-discharge cycles can be prevented to the possible extent. Particularly when the open pore ratio is adjusted to 70% or higher, stress release is more readily attained, to thereby effectively prevent grain boundary cracking. In addition, since the bonding strength of the boundary between the plate-like particle 15 b 2 of cathode active material and the binder 15 b 1 is enhanced, the aforementioned interface separation is effectively prevented. Thus, according to the sintered sheets of Experiment Examples 1-1 to 1-7, the capacity of the cell employing each sintered sheet can be enhanced, while favorable cycle characteristic is maintained.

Furthermore, when an electrolyte permeates an open pore, the inner wall of the open pore favorably serves as a lithium intercalation/deintercalation face. Therefore, through controlling the open pore ratio to 70% or higher, the rate characteristic is improved, as compared with the case of a high closed pore ratio.

In contrast, when the voidage is lower than 3% (Experiment Example 1-8) or the open pore ratio is lower than 70% (Experiment Example 1-9), the stress releasing effect by pores (grain boundary cracking prevention effect) and interface separation prevention effect are insufficient. Actually, the cycle characteristic was considerably impaired.

Next, the ratio of intensity of X-ray diffraction by the (003) plane to intensity of X-ray diffraction by the (104) plane; i.e., the peak intensity ratio [003]/[104] was evaluated. XRD (X-ray diffraction) was carried out though the following procedure.

Specifically, a ceramic sheet for the cathode active material layer, which had been worked to a φ of about 5 to about 10 mm, was placed on a sampler holder for XRD. By means of an XRD apparatus (RINT-TTR III, product of Rigaku Corp.), the surface of the ceramic sheet for the cathode active material layer was irradiated with X-ray so as to measure an XRD profile, thereby obtaining the ratio of intensity (peak height) of diffraction by the (003) plane to intensity (peak height) of diffraction by the (104) plane, [003]/[104]. Thus, according to the above-mentioned method, there is obtained a profile of diffraction by crystal faces present in parallel with crystal faces of the plate surface; i.e., a profile of diffraction by crystal faces oriented in a plate surface direction.

In order to evaluate the influence of the peak intensity ratio [003]/[104], sintered sheet samples of Experiment Examples 1-10 to 1-14, which had the same voidage and open pore ratio but varied orientation degrees, were produced. In Experiment Examples 1-10 to 1-14, the same raw material particle size and firing temperature for yielding an intermediate fired product as employed in Experiment Example 1-5 were employed, whereby the same voidage and open pore ratio (voidage: 8.2%, open pore ratio; 98%) as employed in Experiment Example 1-5 were realized. However, lithium introduction conditions (i.e., type and amount of lithium compound, and treatment temperature: see, Table 3) were appropriately modified, to thereby vary the orientation degree. Table 4 shows the results.

TABLE 3 Li/M Li incorporation temp. Li compd. mole ratio (° C.) Exp. Ex. 1-10 Li₂O₂ 1 775 Exp. Ex. 1-11 LiNO₃ 1 800 Exp. Ex. 1-12 LiNO₃ 1.2 840 Exp. Ex. 1-13 Li₂CO₃ 5 870 Exp. Ex. 1-14 Li₂CO₃ 10 900

TABLE 4 Open pore [003]/[104] Percent capacity Voidage ratio peak intensity maintenance (%) (%) ratio (%) Exp. Ex. 1-10 8.2 98 0.6 98 Exp. Ex. 1-11 8.2 98 0.8 97 Exp. Ex. 1-12 8.2 98 1.6 95 Exp. Ex. 1-13 8.2 98 6 81 Exp. Ex. 1-14 8.2 98 10 70

As is clear from Table 4, in Experiment Examples 1-10 to 1-12, in which the peak intensity ratio [003]/[104] was 2 or lower, excellent cycle characteristic was attained. In contrast, in Experiment Examples 1-13 and 1-14, in which the peak intensity ratio [003]/[104] was in excess of 2, cycle characteristic was impaired, as compared with Experiment Examples 1-10 to 1-12, in which the peak intensity ratio [003]/[104] was 2 or lower.

When the plate-like particle 15 b 2 of cathode active material of the embodiment has a structure in which numerous primary particles (crystal particles) have been bound to one another. Thus, in order to evaluate the influence of the primary particle size, there were produced ceramic sheet samples of Experiment Examples 1-15 to 1-19 having different primary particle sizes at a constant voidage and pore size. In Experiment Examples 1-15 to 1-19, the ceramic sheet samples having different primary particle sizes were formed by appropriately modifying conditions employed in incorporation of lithium (i.e., type and amount of lithium compound and treatment temperature, see Table 5), while the voidage and pore size were maintained by controlling, to constant values, the raw material particle size and firing temperature for yielding an intermediate fired product.

TABLE 5 Li/M Li incorporation temp. Li compd. mole ratio (° C.) Exp. Ex. 1-15 Li₂O₂ 1 775 Exp. Ex. 1-16 LiNO₃ 1 800 Exp. Ex. 1-17 LiNO₃ 1.2 840 Exp. Ex. 1-18 LiNO₃ 2 870 Exp. Ex. 1-19 LiNO₃ 3 900

The primary particle size was determined through the following procedure. Specifically, a sample for observation under an electron microscope was prepared by thinning a ceramic sheet for a cathode active material layer to a thickness of about 80 nm through FIB (focused ion beam) working. The sample had a cross section in parallel with the plate surface of the ceramic sheet. The magnification of the transmission electron microscope was adjusted so that 10 or more primary particles were included in a vision field, and a bright image of the sample was taken. An inscribed circle was drawn in each of the 10 primary particles observed in the bright image, and the diameter of the inscribed circle was determined. The thus-obtained diameters were averaged, to thereby obtain a primary particle size. The evaluation results of Experiment Examples 1-15 to 1-19 are shown in Table 6.

TABLE 6 Open pore Primary Percent capacity Voidage ratio particle size maintenance (%) (%) (μm) (%) Exp. Ex. 1-15 8.2 98 0.3 98 Exp. Ex. 1-16 8.2 98 1.4 96 Exp. Ex. 1-17 8.2 98 2 95 Exp. Ex. 1-18 8.2 98 6 70 Exp. Ex. 1-19 8.2 98 8 65

As is clear from Table 6, the ceramic sheet samples of Experiment Examples 1-15 to 1-17, having a primary particle size of 5 μm or less, exhibited a favorable cycle characteristic. In contrast, the ceramic sheet sample of Experiment Examples 1-18 and 1-19, having a primary particle size in excess of 5 μm, exhibited an impaired cycle characteristic.

Example 2

<<Specific Example 2: Nickel-based composition>>

Also, producing conditions in Experiment Examples 2-1 to 2-9, where the plate-like particles 15 b 2 of cathode active material is Li(Ni, Co, Al)O₂ ceramic particles, are shown in Table 7.

TABLE 7 Pore-forming Material Intermediate material particle size firing temp. shape/amount Process (μm) (° C.) (wt. parts) Exp. Ex. One-step fibrous/5 2-1 Exp. Ex. Two-step 0.3 1,100 0 2-2 Exp. Ex. Two-step 0.3 1,100 fibrous/5 2-3 Exp. Ex. Two-step 0.5 1,000 0 2-4 Exp. Ex. Two-step 1.0 1,000 fibrous/5 2-5 Exp. Ex. One-step fibrous/7.5 2-6 Exp. Ex. One-step fibrous/12.5 2-7 Exp. Ex. One-step fibrous/2.5 2-8 Exp. Ex. One-step spherical/5 2-9

The detailed production conditions employed in Experiment Examples 2-2 and 2-4 shown in Table 7 are as follows (two-step process, no pore-forming material).

(1) Preparation of Slurry

NiO powder (particle size: 1 to 10 μm; product of Seido Kagaku Kogyo Co., Ltd.) (75.1 parts by weight), CO₃O₄ powder (particle size: 1 to 5 μm; product of Seido Kagaku Kogyo Co., Ltd.) (21.5 parts by weight), and Al₂O₃ powder (particle size: 1 to 10 μm; product of Showa Denko K.K.) (3.4 parts by weight) were mixed together and pulverized, and the resultant mixture was thermally treated in air at 1,000° C. for five hours, to thereby synthesize (Ni_(0.75), CO_(0.2), Al_(0.05))O powder.

The thus-synthesized powder was pulverized by means of a pot mill, and the resultant (Ni_(0.75), CO_(0.2), Al_(0.05))O raw material particles (100 parts by weight) were mixed with a dispersion medium (toluene:isopropanol=1:1) (100 parts by weight), a binder (polyvinyl butyral: product No. “BM-2,” product of Sekisui Chemical Co. Ltd.) (10 parts by weight), a plasticizer (DOP: di(2-ethylhexyl) phthalate, product of Kurogane Kasei Co., Ltd.) (4 parts by weight), and a dispersant (trade name “RHEODOL SP-O30,” product of Kao Corporation) (2 parts by weight). The resultant mixture was stirred under reduced pressure for defoaming, and the viscosity thereof was adjusted to 3,000 to 4,000 cP.

(2) Sheet Forming

The thus-prepared slurry was formed into a sheet-like compact on a PET film through the doctor blade method so that the thickness of the compact as measured after drying was adjusted to 20 μm.

(3) Calcination

The sheet-like compact was removed from the PET film. 20 g of compact was crumpled and placed in a sheath made of alumina (dimensions: 150 mm square×10 mm in height), and then heated in air at a specific temperature (firing temperature for yielding an intermediate fired product) for 3 hours. Thereafter, the piece was cooled at 200 degrees (° C.)/h to room temperature. Then, a portion of the piece which was not fused to the sheath was picked up.

(4) Pulverization

The thus-removed fired compact (50 g), nylon balls (diameter: 10 mm) (370 g), and ethanol (165 g) were placed in a polypropylene-made pot (volume: 1 L) and mixed for 20 hours for pulverization.

(5) Lithium Incorporation

The thus-obtained (Ni_(0.75), Co_(0.2), Al_(0.05))O powder was mixed with Li₂CO₃ powder (product of Kanto Chemical Co., Inc.) so that Li/Co was 1.1, and the mixture was thermally treated in an oxygen atmosphere (0.1 MPa) at 825° C. for 24 hours, to thereby produce plate-like Li_(1.0)(Ni_(0.75), Co_(0.2), Al_(0.05))O₂ powder particles (plate-like particles 15 b 2 of cathode active material) having a thickness of 20 μm.

The detailed production conditions employed in Experiment Examples 2-3 and 2-5 shown in Table 7 were the same as those employed in other Experiment Examples (e.g., 2-2), except that the aforementioned pore-forming material was added (two-step process, no pore-forming material). The detailed production conditions employed in Experiment Examples 2-1 and 2-6 to 2-9 shown in Table 7 are as follows (one-step process).

(1) Preparation of Slurry

NiO powder (particle size: 1 to 10 μm; product of Seido Kagaku Kogyo Co., Ltd.), CO₃O₄ powder (particle size: 1 to 5 μm; product of Seido Kagaku Kogyo Co., Ltd.), Al₂O₃.H₂O (particle size: 1 to 3 μm; product of SASOL), and Li₂CO₃ powder (particle size: 10 to 50 μm; product of Kanto Chemical Co., Inc.) were mixed at predetermined proportions so as to attain a composition of Li_(1.50)(Ni_(0.75)Co_(0.2)Al0.05)O₂. From the thus-prepared material powder (100 parts by weight) and the aforementioned pore-forming material, a slurry was prepared through the same procedure as employed in the aforementioned Experiment Examples (viscosity of slurry: 500 to 700 cP).

(2) Sheet Forming

The thus-prepared slurry was formed into a sheet-like compact on a PET film through the doctor blade method so that the thickness of the compact as measured after drying was adjusted to 30 μm.

(3) Calcination

The sheet-like compact was removed from the PET film. 20 g of compact was crumpled and placed in a sheath made of alumina (dimensions: 150 mm square×10 mm in height), and then heated in air at a specific temperature (firing temperature for yielding an intermediate fired product) for 5 hours. Thereafter, the piece was cooled at 200 degrees (° C.)/h to room temperature. Then, a portion of the piece which was not fused to the sheath was picked up, to thereby produce flake-like fired compact.

(4) Pulverization

The thus-removed fired compact (50 g), nylon balls (diameter: 10 mm) (370 g), and ethanol (165 g) were placed in a polypropylene-made pot (volume: 1 L) and mixed for 20 hours for pulverization, to thereby produce plate-like LiCoO₂ powder particles (plate-like particles 15 b 2 of cathode active material) having a thickness of 20 μm.

The plate-like particles of the Experiment Examples shown in Table 7 were evaluated, and the results are shown in Table 8. As is clear from Table 8, the ceramic sheets having a nickel-based composition were found to have the same characteristics as those of the ceramic sheets having a cobalt-based composition.

TABLE 8 Open pore Percent capacity Voidage ratio maintenance (%) (%) (%) Exp. Ex. 2-1 3.2 70 89 Exp. Ex. 2-2 3 80 92 Exp. Ex. 2-3 3.1 95 93 Exp. Ex. 2-4 8 81 89 Exp. Ex. 2-5 7.8 98 95 Exp. Ex. 2-6 9.2 72 88 Exp. Ex. 2-7 29.5 70 91 Exp. Ex. 2-8 2.5 71 45 Exp. Ex. 2-9 3.2 64 57

Similar to the aforementioned LiCoO₂ sheets, lithium oxide ceramic sheets of a nickel-based composition were evaluated in terms of peak intensity ratio [003]/[104] and effect of primary particle size. The results are shown in Tables 9 to 12. As is clear from Tables 9 to 12, the ceramic sheets having a nickel-based composition were found to have the same characteristics as those of the aforementioned LiCoO₂ sheets.

TABLE 9 Li/M Li incorporation temp. Li compd. mole ratio (° C.) Exp. Ex. 2-10 Li₂O₂ 2 750 Exp. Ex. 2-11 Li₂O₂ 3 750 Exp. Ex. 2-12 LiOH 3 775 Exp. Ex. 2-13 LiOH 5 800 Exp. Ex. 2-14 LiOH 10 800

TABLE 10 Open pore [003]/[104] Percent capacity Voidage ratio peak intensity maintenance (%) (%) ratio (%) Exp. Ex. 2-10 7.8 98 0.4 97 Exp. Ex. 2-11 7.8 98 0.5 96 Exp. Ex. 2-12 7.8 98 1.4 95 Exp. Ex. 2-13 7.8 98 6 80 Exp. Ex. 2-14 7.8 98 9 75

TABLE 11 Li/M Li incorporation temp. Li compd. mole ratio (° C.) Exp. Ex. 2-15 Li₂O₂ 2 750 Exp. Ex. 2-16 Li₂O₂ 3 750 Exp. Ex. 2-17 LiOH 3 775 Exp. Ex. 2-18 LiOH 5 800 Exp. Ex. 2-19 LiOH 10 800

TABLE 12 Open pore Primary Percent capacity Voidage ratio particle size maintenance (%) (μm) (μm) (%) Exp. Ex. 2-15 7.8 98 0.2 98 Exp. Ex. 2-16 7.8 98 0.6 96 Exp. Ex. 2-17 7.8 98 0.9 95 Exp. Ex. 2-18 7.8 98 4 73 Exp. Ex. 2-19 7.8 98 7 65 <Examples of Modifications>

The above-described embodiment and specific examples are, as mentioned above, mere examples of the best mode of the present invention which the applicant of the present invention contemplated at the time of filing the present application. The above-described embodiment and specific examples should not be construed as limiting the invention. Various modifications to the above-described embodiment and specific examples are possible, so long as the invention is not modified in essence.

Several modifications will next be exemplified. In the following description of the modifications, component members similar in structure and function to those of the above-described embodiment are denoted by names and reference numerals similar to those of the above-described embodiment. The description of the component members appearing in the above description of the embodiment can be applied as appropriate, so long as no inconsistencies are involved.

Needless to say, even modifications are not limited to those described below. Limitingly construing the present invention based on the above-described embodiment and the following modifications impairs the interests of an applicant (particularly, an applicant who is motivated to file as quickly as possible under the first-to-file system) while unfairly benefiting imitators, and is thus impermissible.

The structure of the above-described embodiment and the structures of the modifications to be described below are entirely or partially applicable in appropriate combination, so long as no technical inconsistencies are involved.

The present invention is not limited to the constitution which is specifically disclosed in the description of the above embodiments. For example, the cathode collector 15 a of the cathode 15 may be omitted.

The ratio by mole of lithium to M; i.e., Li/M (Li/Co or Li/(Co, Ni, Mn)) of a sintered sheet represented by formula Li_(x)MO₂ is not limited to 1.0. However, the ratio is preferably 0.9 to 1.2, more preferably 1.0 to 1.1. Through controlling the ratio, excellent charge-discharge capacity is attained.

Needless to say, those modifications which are not particularly referred to are also encompassed in the technical scope of the present invention, so long as the invention is not modified in essence.

Those components which partially constitute means for solving the problems to be solved by the present invention and are illustrated with respect to operations and functions encompass not only the specific structures disclosed above in the description of the above embodiment and modifications but also any other structures that can implement the operations and functions. Further, the contents (including specifications and drawings) of the prior application and publications cited herein can be incorporated herein as appropriate by reference. 

What is claimed is:
 1. A plate-like particle of a cathode active material for a lithium secondary battery, wherein the plate-like particle has a structure in which numerous primary particles are bound to one another, each primary particle having a layered rock salt structure, wherein the plate-like particle has a thickness of 5 μm or more and less than 30 μm, a ratio of intensity of X-ray diffraction by the (003) plane to intensity of X-ray diffraction by the (104) plane, [003]/[104], of 2 or less, a voidage of 3% or more and less than 30%, and an open pore ratio of 70% or higher, wherein the intensity of X-ray diffraction is attained by measuring an X-ray diffraction profile of only a plate surface of the plate-like particle.
 2. The plate-like particle of a cathode active material according to claim 1, wherein the plate-like particle has a ratio w/t of 3 or more, wherein t represents the thickness of the plate-like particle, and wherein w represents the minimum size of the plate-like particle as measured in a direction orthogonal to the thickness direction which defines the thickness t.
 3. The plate-like particle of a cathode active material according to claim 1, wherein the primary particles have a primary particle size of 5 μm or less.
 4. A cathode of a lithium secondary battery having a cathode active material layer which contains a plate-like particle having a structure in which numerous primary particles are bound to one another, wherein the plate-like particle has a thickness of 5 μm or more and less than 30 μm, a ratio of intensity of X-ray diffraction by the (003) plane to intensity of X-ray diffraction by the (104) plane, [003]/[104], of 2 or less, a voidage of 3% or more and less than 30%, and an open pore ratio of 70% or higher, and wherein the intensity of X-ray diffraction is attained by measuring an X-ray diffraction profile of only a plate surface of the plate-like particle.
 5. The cathode of a lithium secondary battery according to claim 4, wherein the plate-like particle has a ratio w/t of 3 or more, wherein t represents the thickness of the plate-like particle, and wherein w represents the minimum size of the plate-like particle as measured in a direction orthogonal to the thickness direction which defines the thickness t.
 6. The cathode of a lithium secondary battery according to claim 4, wherein the primary particles have a primary particle size of 5 μm or less.
 7. The cathode of a lithium secondary battery according to claim 4, wherein the cathode active material layer comprises a binder and the plate-like particles and an electroconducting aid dispersed in the binder.
 8. A lithium secondary battery comprising at least: a cathode having a cathode active material layer which contains a plate-like particle having a structure in which numerous primary particles are bound to one another, each primary particle having a layered rock salt structure, wherein the plate-like particle has a ratio of intensity of X-ray diffraction by the (003) plane to intensity of X-ray diffraction by the (104) plane, [003]/[104], of 2 or less, a thickness of 5 μm or more and less than 30 μm, a voidage of 3% or more and less than 30%, and an open pore ratio of 70% or higher, and wherein the intensity of X-ray diffraction is attained by measuring an X-ray diffraction profile of only a plate surface of the plate-like particle; an anode containing a carbonaceous material or a lithium-occluding substance as an anode active material; and an electrolyte disposed so as to intervene between the cathode and the anode.
 9. The lithium secondary battery according to claim 8, wherein the plate-like particle has a ratio w/t of 3 or more, wherein t represents the thickness of the plate-like particle, and wherein w represents the minimum size of the plate-like particle as measured in a direction orthogonal to the thickness direction which defines the thickness t.
 10. The lithium secondary battery according to claim 8, wherein the primary particles have a primary particle size of 5 μm or less.
 11. The lithium secondary battery according to claim 8, wherein the cathode active material layer comprises a binder and the plate-like particles and an electroconducting aid dispersed in the binder.
 12. The plate-like particle according to claim 1, wherein the plate-like particle has the ratio [003]/[104] of intensity of X-ray diffraction of 0.8 or less.
 13. The cathode of a lithium secondary battery according to claim 4, wherein the plate-like particle has the ratio of [003]/[104] of intensity of X-ray diffraction of 0.8 or less.
 14. The lithium secondary battery according to claim 8, wherein the plate-like particle has the ratio [003]/[104] of intensity of X-ray diffraction of 0.8 or less. 